Name | Type | Viscosity (25℃) | Geltime (min.) | Characteristics and applications |
BY-1712 | Ortho | 280-360 | 25-35 | Pre-accelerated, medium viscosity, good glass fiber wet-out characteristic, suitable for general purpose. |
BY-1713 | Ortho | 140-180 | - | Medium reactivity, pre-accelerated, low viscosity, long geltime, containing curing indicator, good glass fiber wet-out, high mechanical property. Suitable for FRP cabin cover, cooling towers with larger dimension by RTM or VARTM. |
BY-1714 | Ortho | 100-150 | - | Pre-accelerated, low viscosity, long geltime, good glass fiber wet-out, relatively high heat resistance and good mechanical properties. Suitable for FRP cabin cover, cooling towers with larger dimension by RTM or VARTM. Approved by CCS for boat building. |
BY-1715 | Ortho | 170-200 | 80-110 | Pre-accelerated, low viscosity, long geltime, good glass fiber wet-out, relatively high heat resistance and good mechanical properties. Specially designed for wind mill blades by RTM or VARTM. |
BY-1716 | Ortho | 300-500 | 70-110 | Pre-accelerated, thixotropic, low volatilization, long geltime, exothermic peak is low, good heat resistance, high mechanical strength and toughness. Suitable for hand lay-up, spray-up wind blades or other larger dimension FRP products. |
BY-1718 | Ortho | 140-180 | - | Medium reactivity, pre-accelerated, low viscosity, long geltime, containing curing indicator, good glass fiber wet-out, high mechanical property. Suitable for FRP cabin cover, cooling towers with larger dimension by RTM or VARTM. |
BY-1719 | Ortho | 170-230 | - | Pre-accelerated, low viscosity, long geltime, good glass fiber wet-out, relatively high heat resistance and good mechanical properties. Suitable for RTM and VARTM to produce parts of vehicles, yachts, cooling towers and other FRP products. |
BY-1710 | ISO | 260-330 | 25-35 | Medium reactivity, pre-accelerated, low viscosity, good glass fiber wet-out, good chemical resistance and mechanical properties. Suitable for automotive parts, boat building, cooling towers etcby RTM or VARTM. |
BY-1711 | PTA | 90-120 | - | Pre-accelerated, thixotropic, well-spliced with acrylic. Suitable for hand lay-up and spray-up FRP reinforcement parts for acrylic sanitary wares. |
BY-1720 | VE | 100-150 | - | Bisphone A type vinyl ester resin. High mechanical strength and toughness, low shrinkage. Suitable for RTM, VARTM, hand lay-up, twine and etc. |